Product Details
Place of Origin: Shanghai
Brand Name: TANKII
Certification: ISO9001
Model Number: X8cral 20-6
Payment & Shipping Terms
Minimum Order Quantity: 50kg
Packaging Details: to wind with thin film, bubble film,carton,wooden pallet or case
Delivery Time: 8-15 days
Payment Terms: L/C, T/T, Western Union
Supply Ability: 90+ton+per month
Material: |
Fecral |
Condition: |
Soft Annealed |
Surface: |
Bright |
Shape: |
Foil,strip,sheet |
Material: |
Fecral |
Condition: |
Soft Annealed |
Surface: |
Bright |
Shape: |
Foil,strip,sheet |
X8cral 20-6 fecral alloy Catalytic Converter Foil for Heat Element
Fecral alloy is high resistance and electrical heating alloy. Fecral alloy can reach process temperature of 2192 to 2282 F, corresponding to oa resistance temperature of 2372 F.
It is normally used in electrical furnace, glass top hobs, quartz tube heaters, resistors, catalytic converter,heating elements etc.
Nominal Analysis
21.00 Cr, 6.00 Al, Bal. Fe
Max contineous working temperature: 1250º C.
Melting Temperature: 1500º C
Thickness 0.05~0.1mm, width 1-1000mm
Usage: Catalytic converters
Material 1.4767, DIN 17470
Brand name | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
Main chemical composition% | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 22.5-24.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.0 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
RE | opportune amount |
opportune amount |
opportune amount |
opportune amount |
opportune amount |
opportune amount |
opportune amount |
|
Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest | |
Nb0.5 | Mo1.8-2.2 | |||||||
Max.continuous service temp.of element (ºC) |
950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
Resistivity μΩ.m,20ºC |
1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
Density (g/cm3 ) |
7.4 | 7.10 | 7.16 | 7.25 | 7.35 | 7.10 | 7.10 | |
Thermal conductivity KJ/m.h.ºC |
52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | 45.2 | |
Coefficient of lines expansion α×10-6/ºC |
15.4 | 16.0 | 14.7 | 15.0 | 13.5 | 16.0 | 16.0 | |
Melting pointºC | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
Tensile strength Mpa |
580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
Elongation at rupture % |
>16 | >12 | >12 | >12 | >12 | >12 | >10 | |
Variation of area % |
65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
Repeat bending frequency(F/R) |
>5 | >5 | >5 | >5 | >5 | >5 | >5 | |
Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
Micrographic structure |
Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
Magnetic properties |
Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |